Waterproofing system primer coat - SEALCOAT-PRIMERBUILDINGSEALANT-10L

Waterproofing system primer coat

Name: Waterproofing system primer coat
Brand: Würth
SKU: 0893212100

Primer coat waterproofing system
SEALCOAT-PRIMERBUILDINGSEALANT-10L

Art.-no. 0893212100

EAN 4058794712476

All versions

Prices for customers after login

Waterproofing system primer coat

Art.-no. 0893212100

Prices for customers after login

Quantity

x 1 pcs

Exclusively for trade customers

Login/Register
Call customer service:

Surface pre-treatment under bituminous and cement-based building waterproofing systems

Can be used on saline and problematic surfaces

Can be used on sandstone

Wide range of applications, one product for many applications

High application reliability

Can be used on surfaces in old and new buildings

Wide range of applications, therefore easy, safe use on construction sites

Penetrates surfaces well

Has a strengthening effect deep into the surface

Stabilises the surface

Creates an adhesive bridge between the surface and the seal

Reduces pores, thereby prevents salts from re-forming on the wall surface

Effective at protecting the surface against chemical and mechanical stresses

Ready for use, fast-drying

Can be applied directly, does not need to be stirred or thinned, resulting in secure, time-saving application

Solvent-free

Notice

Glass surfaces (windows or similar) must be protected from contact with the building waterproofing system primer coat, as contact may cause discolouration. During application, we recommend using personal protective equipment (safety goggles/gloves) occupational safety reasons. Clean with water immediately after use.

Application area

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Product information

Würth Catalogue

Datasheets(X)

Certificates/ Documents

Application area

Suitable for mineral surfaces (except for plaster), mortar, mineral plaster, cement-based sludge, brick, sand-lime brick and concrete in the areas of renovations and new buildings. Can be used in the Würth building waterproofing system to strengthen the surface and as an adhesion agent when bituminous (art. no. 0893 212 115/0893 212 120) and cement-based seals (art. no. 0893 212 125) are used. For reducing water absorption; also suitable for problematic surfaces such as sandstone.

Instructions

The surface must be free from oil, and must be cleaned of loose components. Salt efflorescence must be removed with a brush. Apply undiluted primer to the surface to be coated using the swab, brush or roller. The areas must be saturated to achieve effective priming. Highly absorbent surfaces (e.g. aerated concrete) must be primed twice. The primed surfaces can be worked with bituminous seals after approx. 12 hours and with cement-based seals after approx. 30 minutes.

Contents	10 l
Chemical basis	Polymer/silicate
Density	1.03 g/cm³
Min. processing temperature	5 °C
Max. processing temperature	30 °C
Min./max. surface processing temperature	5 to 30 °C
Min. surface processing temperature	5 °C
Max. surface processing temperature	30 °C
Min./max. processing temperature	5 to 30 °C
Application quantity in weight/area	0.13 kg/m²
Application quantity in weight/area/conditions	0.13 kg/m² / with absorbent surfaces, e.g. aerated concrete: double coat
Application quantity conditions	with absorbent surfaces, e.g. aerated concrete: double coat
pH value	11.5
Viscosity	175 mPas
Further processing conditions	bituminous material
Can be further processed after	12 h
Solvent-free	Yes
Additional articles	Universal brush, art. no. 0693009...

Can be further processed after	approx. 12 hours	For bituminous material
Can be further processed after	approx. 30 min	For cementitious material

Suitable glove:

Product

Description

Nitrile chemical protective glove With cotton velour finish inside

Description:

Permeation level: 6

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time

Permeation level

< 10 min

≥ 10 min

≥ 30 min

≥ 60 min

≥ 120 min

≥ 240 min

≥ 480 min

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.